    Properties of NaxCoO2 /

    • CSV
    • RefMan
    • EndNote
    • BibTex
    • RefWorks
    Thumbnail
    Name:
    Brock_Jalili_Helia_2005.pdf
    Size:
    3.780Mb
    Format:
    PDF
    Download
    Author
    Jalili, Helia.
    Keyword
    Sodium cobalt oxide
    Sodium cobalt oxide
    Superconductors.
    Thermoelectric materials.
    
    Metadata
    Show full item record
    URI
    http://hdl.handle.net/10464/1647
    Abstract
    Polycrysttdline samples of NaiCoOa were prepared using the "Rapid heat-up" method. One set of samples was annealed in flowing O2, while the other set in flowing Argon. X-Ray diffraction measurements indicated a stable phase of Nao.7Co02 mixed with C03O4 for all the samples even though they differed in concentration of Na. Argon annealed samples were insulators, whereas the ones annealed in O2 were metallic. Most of the measurements were performed on the sample Nao.7Co02, because it is the host compound for the superconductor sample Nao.35Co02-H20. Magnetization measurement showed that the magnetic moment decreased with increasing sodium concentration. This is due to the existence of C03O4 in samples with Na^ 0.7. As sodium concentration decreases, the magnetic moment increases due to the increasing concentration of C03O4 and its large magnetic moment. Magnetization measurements showed that the magnetic moment of Nao.7Co02 is field-dependent in low fields eind field-independent in fields higher than 100 G. Resistivity changes with temperature (dp/dT) increased with increasing Na concentration. Also resistivity measurements were performed under different hydrostatic pressures on Nao.7Co02. Two transitions were observed; one at a temperature Ti ~20 K and the other at T2 ^280 K, the transition at Ti has a magnetic origin and the one at T2 is a structiural transition. It was noticed that pressure aJfects resistivity of the sample. At higher pressures resistivity changes faster with temperature. Magnetoresistance measurement showed a small change in the resistivity, especially at lower temperatures. A novel layered superconductor Nao.35Co02H20 was prepared using de-intercalation of Na from the host compound Nao.7Co02. FVom the temperature dependence of the magnetization, the superconducting transition temperature and lower critictil field have been estimated as Tc=4.12 K and Hci=66 G, respectively.
    Collections
    M.Sc. Physics

    entitlement

     
    DSpace software (copyright © 2002 - 2022)  DuraSpace
    Quick Guide | Contact Us
    Open Repository is a service operated by 
    Atmire NV
     

    Export search results

    The export option will allow you to export the current search results of the entered query to a file. Different formats are available for download. To export the items, click on the button corresponding with the preferred download format.

    By default, clicking on the export buttons will result in a download of the allowed maximum amount of items.

    To select a subset of the search results, click "Selective Export" button and make a selection of the items you want to export. The amount of items that can be exported at once is similarly restricted as the full export.

    After making a selection, click one of the export format buttons. The amount of items that will be exported is indicated in the bubble next to export format.